产品规格
公称外径(mm) | PE80 | PE100 | ||
SDR17.6 | SDR11 | SDR17.6 | SDR11 | |
公称压力≦0.2MPa | 公称压力≦0.4MPa | 公称压力≦0.6MPa | 公称压力≦1.0MPa | |
壁厚 (mm) | 壁厚 (mm) | 壁厚 (mm) | 壁厚 (mm) | |
20 | 2.3 | 3.0 | 2.3 | 3.0 |
25 | 2.3 | 3.0 | 2.3 | 3.0 |
32 | 2.3 | 3.0 | 2.3 | 3.0 |
40 | 2.3 | 3.7 | 2.3 | 3.7 |
50 | 2.9 | 4.6 | 2.9 | 4.6 |
63 | 3.6 | 5.8 | 3.6 | 5.8 |
75 | 4.3 | 6.8 | 4.3 | 6.8 |
90 | 5.2 | 8.2 | 5.2 | 8.2 |
110 | 6.3 | 10.0 | 6.3 | 10.0 |
125 | 7.1 | 11.4 | 7.1 | 11.4 |
140 | 8.0 | 12.7 | 8.0 | 12.7 |
160 | 9.1 | 14.6 | 9.1 | 14.6 |
180 | 10.3 | 16.4 | 10.3 | 16.4 |
200 | 11.4 | 18.2 | 11.4 | 18.2 |
225 | 12.8 | 20.5 | 12.8 | 20.5 |
250 | 14.2 | 22.7 | 14.2 | 22.7 |
280 | 15.9 | 25.4 | 15.9 | 25.4 |
315 | 17.9 | 28.6 | 17.9 | 28.6 |
355 | 20.2 | 32.3 | 20.2 | 32.3 |
400 | 22.8 | 36.4 | 22.8 | 36.4 |
450 | 25.6 | 40.9 | 25.6 | 40.9 |
500 | 28.4 | 45.5 | 28.4 | 45.5 |
560 | 31.9 | 50.9 | 31.9 | 50.9 |
630 | 35.8 | 57.3 | 35.8 | 57.3 |
性能指标
性能 | 要求 |
纵向回缩率, %, (110℃) | <=3 |
氧化诱导时间, min, (200℃) | >=20 |
断裂伸长率,% | >=350 |
炭黑含量(质量分数),%(只适用于黑色混配料) | 2.0~2.5 |
溶体流动速率, g/10min (195℃,5kg) | 与产品标称值的偏差不应超过±20% |
耐气体组分, h(80℃,2Mpa) | ≥20 |
静液压强度 1)20℃, 环向应力:PE100 12.4Mpa, PE809.0Mpa,100h 2)80℃, 环向应力:PE100 5.4Mpa, PE80 4.5Mpa, 165h 3)80℃, 环向应力:PE100 5.0Mpa, PE80,4.0Mpa, 1000h |
通过 通过 通过 |
1.无毒。HDPE材质无毒无味。
2.低阻流。内壁光滑,管道输送方便,在同等使用环境下,HDPE管道的输送能力可提高30%,其粗糙度比钢管和玻璃纤维增强管小很多。
3. 无泄漏。HDPE管连接的方式有热熔对接、承插对接和电熔,这意味着连接点的强度比管本身高。
4.灵活性强。小口径高密度聚乙烯管可以盘管,大口径管材也可以轻微弯曲,施工更加方便。
5.抗挠性好。HDPE管的耐磨性是钢管的4倍,这意味着HDPE管道的使用寿命更长,更经济实用。
6.施工方便。PE管可以安装在各种非开挖工程中,便于施工和安装。
7.寿命长。在额定温度和压力下实用寿命为50年。
8.降低操作和维护成本。高密度聚乙烯管道不仅便于运输和安装,而且大大降低了工人的劳动强度,提高了工作效率。
燃气用埋地聚乙烯管道适用于工作温度在-20℃ ~~-40℃,长期最大工作压力不大于0.7MPA的燃气输送用管道系统。